▼a Investigating Microstructural Effects on Short Crack Growth and Fatigue Life Behavior of WE43 Magnesium. |
| 260 | |
▼a [S.l.]:
▼b University of Michigan.,
▼c 2018. |
| 260 | 1 |
▼a Ann Arbor:
▼b ProQuest Dissertations & Theses,
▼c 2018. |
| 300 | |
▼a 276 p. |
| 500 | |
▼a Source: Dissertation Abstracts International, Volume: 79-12(E), Section: B. |
| 500 | |
▼a Advisers: John Edmond Allison |
| 502 | 1 |
▼a Thesis (Ph.D.)--University of Michigan, 2018. |
| 520 | |
▼a Magnesium alloys are increasingly being used in structural applications due to their excellent strength-to-weight ratio, particularly in applications where reductions in weight can result in significant improvements to fuel efficiency. Extending |
| 520 | |
▼a Crack initiation, short crack growth, and VHCF life behavior have been investigated for three microstructural conditions of WE43 magnesium. As-received (T5) WE43 with a relatively fine grain size was solution treated and aged to produce precipit |
| 520 | |
▼a A number of findings have resulted from these experiments and analyses, providing new insight into the role of local microstructure on fatigue behavior. Heat treatment was shown to have a strong effect on fatigue strength, with the fine-grained, |
| 590 | |
▼a School code: 0127. |
| 650 | 4 |
▼a Materials science. |
| 690 | |
▼a 0794 |
| 710 | 20 |
▼a University of Michigan.
▼b Materials Science and Engineering. |
| 773 | 0 |
▼t Dissertation Abstracts International
▼g 79-12B(E). |
| 773 | |
▼t Dissertation Abstract International |
| 790 | |
▼a 0127 |
| 791 | |
▼a Ph.D. |
| 792 | |
▼a 2018 |
| 793 | |
▼a English |
| 856 | 40 |
▼u http://www.riss.kr/pdu/ddodLink.do?id=T15000477
▼n KERIS
▼z 이 자료의 원문은 한국교육학술정보원에서 제공합니다. |
| 980 | |
▼a 201812
▼f 2019 |
| 990 | |
▼a ***1012033 |